Copper Based

home > 재료소개(Powder/Wire) > Powder-Pure Metals and Metal Alloys >Copper Based

Advanced alloy powders, pure and simple

From simple coatings for buildup repair to complex coatings that protect against high-temperature wear and oxidation, we offer a wide range of pure metal-based alloy powders. We use a variety of manufacturing techniques—including argon gas atomization (AGA), vacuum sintering, agglomeration and physical blending—to produce standard and custom powders that deliver the coating properties your application demands.

Powder Name&Composition Chemistry & Size DIAMETER Safety Data Sheet (SDS)
CU-101

CuNiIn

(Atomized)
Ni 36.5

In 5.0

Co balance

-45 µm/+5 µm
  • Excellent anti-fretting coating
  • Dense coatings with low porosity and oxide content
CU-101 (132KB)
CU-102

CuNiIn

(Atomized)
Ni 36.5

In 5.0

Cu balance

-75 µm/+45 µm
  • Excellent anti-fretting coating
  • Dense coatings with low porosity and oxide content
CU-102 (132KB)
CU-103

Cu-38Ni

(Atomized)
Ni 38.0

Cu balance

75 µm/+45 µm
  • Protects against fretting and galling
  • Dense coatings with low oxide content
CU-103 (132KB)
CU-116

Cu-38Ni

(Atomized)
Ni 38.0

Cu balance

-45 µm
  • Protects against fretting and galling
  • Dense coatings with low oxide content
U-116 (132KB)
CU-104

Cu-10AI-1Fe

(Al-Bronze)

(Atomized)
AI 10.0

Fe 1.0

Cu balance

-53 µm/+5 µm
  • Good bearing material
  • Resistant to fretting and galling at low temperatures
  • Easily machined coating
CU-104 (120KB)
CU-104-2

Cu-10AI-1Fe

(Al-Bronze)

(Atomized)
AI 10.0

Fe 1.0

Cu balance

-53 µm/+11 µm
  • Good bearing material
  • Resistant to fretting and galling at low temperatures
  • Easily machined coating
CU-104-2 (120KB)
CU-104-5

Cu-10AI-1Fe

(Al-Bronze)

(Atomized)
AI 10.0

Fe 1.0

Cu balance

-125 µm/+45 µm
  • Good bearing material
  • Resistant to fretting and galling at low temperatures
  • Easily machined coating
CU-104-5 (120KB)
CU-159-3

Pure Cu

(Atomized)
Cu

99.0 min

-38 µm/+11 µm
  • Atomized, pure Cu
CU-159-3 (120KB)
CU-159

Pure Cu

(Atomized)
Cu

99.0 min

-31 µm/+5 µm
  • Atomized, pure Cu
CU-159 (120KB)
CU-159-1

Pure Cu

(Atomized)
Cu

99.0 min

-75 µm/+45 µm
  • Atomized, pure Cu
CU-159-1 (120KB)